JKN-FL-96S reduces the slurry cake permeability by the aggregation of water-soluble high polymer molecular chain.
Inquiry
Product Description
JKN-FL-96S reduces the slurry cake permeability by the aggregation of water-soluble high polymer molecular chain. And a variety of functional groups are introduced into the polymer to enhance the anti high temperature property and salt resistance.
Characteristics
JKN-FL-96S is polymerized by AMPS, low molecular amide, multi hydroxy carboxylic acid, auxiliary solvent,etc.
Anti temperature property: 30～100℃.
Anti salt property:fresh water until saturated brine.
Water solubility:dissolved in water easily.
Filtration property: ≤100ml API FL.
Generally dosage range: 0.6~0.8% (BWOC).
Good compatibility with other additives.
Compatibility with cement: suitable for all levels of oil well cement.
The cement slurry thickening transition time is short, close to right angle thickening.
Suitable for low, conventional and high density cement slurry system.
Having a little retarding property to the cement slurry.
Technical Specification
Items | Specification |
Appearance | Free flowing powder or particles |
Water content,% | ≤8.0 |
Fineness (0.315mm sieve),% | ≤15.0 |
Initial consistency , Bc/80℃,46.5MPa,45min | ≤30.0 |
Mutation value of thickening curve,Bc | ≤10.0 |
Transition time, min | ≤40.0 |
Fluid loss,ml/80℃,6.9MPa,30min | ≤150.0 |
Free liquid,% | ≤1.4 |
Compression strength, MPa/102℃,21MPa,24h | ≥14.0 |
The ingredient of the cement in the table is: JiaHua G class cement:800g, tap-water:352ml,
Dosage of JKN-FL-96S: 0.8% (BWOC).
Packing, Storage
Sacked with three-layer plastics bag, 25kg per bag.
Be kept away from moisture and possible damage of the packages in transportation, and stored in cool and dry situation.
Storage life time is two years.